WELDING-Wire
|
||
M.I.G.(Metal Inert Gas) - Points to Remember
|
||
|
||
|
||
|
||
|
||
1. Mig (GMAW) welding is often referred to
|
||
by the manufacturer's trade name as Micro-wire,
|
||
Aircomatic, Sigma, and Millermatic Welding.
|
||
|
||
|
||
2. Mig welding is faster than stick electrode
|
||
welding and is much easier to learn.
|
||
|
||
|
||
3. Spray transfer type of welding is particu-
|
||
larly adapted for welding heavy gage metals.
|
||
|
||
|
||
4. Short circuiting transfer welding is best
|
||
for welding light gage metals.
|
||
|
||
|
||
5. For optimum efficiency, DCRP current is
|
||
required for Mig welding.
|
||
|
||
|
||
6. For Mig welding, a constant potentiaI
|
||
power supply with a nearly flat volt-ampere char-
|
||
acteristic produces the best results.
|
||
|
||
|
||
7. As a general rule, an air-cooled gun is
|
||
satisfactory when welding with amperage
|
||
around 200 and a water-cooled gun for welding
|
||
heavy metals requiring higher amperages.
|
||
|
||
|
||
8. The use of CO2 as a shielding gas is most
|
||
effective and less expensive when welding steel.
|
||
|
||
|
||
9. Argon or a mixture of argon and oxygen
|
||
will produce the most effective results in welding
|
||
aluminum and stainless steel.
|
||
|
||
|
||
10. The rate of gas flow for welding most
|
||
metals is approximately 35 cu ft/hr. However,
|
||
this rate may have to be varied somewhat, de-
|
||
pending on the type, electrode size, and thick-
|
||
ness of metal.
|
||
|
||
|
||
|
||
|
||
|
||
|
||
|
||
11. The effectiveness of the shielding gas is
|
||
often governed by the distance of the gun from
|
||
the workpiece. Generally the gas nozzle should
|
||
not be spaced more than 2" from the workpiece.
|
||
|
||
|
||
12. The use of correct diameter wire electrode
|
||
is necessary for good welds. Check recommen-
|
||
dations for correct electrode diameters.
|
||
|
||
|
||
13. The correct current for welding must often
|
||
be determined by trial. Check recommendations
|
||
for starting current.
|
||
|
||
|
||
14. Be sure the wire feed is set for the amper-
|
||
age which is to be used for welding.
|
||
|
||
|
||
15. For most Mig welding applications, the
|
||
wire stick-out should be about 3/8" to 3/4".
|
||
|
||
|
||
16. Keep the gun properly positioned to insure
|
||
uniform weld with proper penetration.
|
||
|
||
|
||
17. Cold laps will occur if the arc does not
|
||
melt the base metal sufficiently.
|
||
|
||
|
||
18. Check the weld for surface porosity. Sur-
|
||
face porosity is usually caused by improper gas
|
||
shielding.
|
||
|
||
|
||
19. Do not remove the gun from the weld area
|
||
until the puddle has solidified, otherwise cracks
|
||
may develop.
|
||
|
||
|
||
20. Remember, insufficient or excessive pene-
|
||
tration is the result of failure to control heat
|
||
input.
|
||
|
||
|
||
|