Charging batteries
|
||
after reading some of the messages under "battery help",I thought I might
|
||
be able to clear up some of the popular misconceptions about batteries.
|
||
Many of the problems blamed on memory or shorted cells are often problems
|
||
resulting from improper charging or discharging.It's a very grey area and
|
||
clearcut answers are hard to find,you will soon find out why!
|
||
One question often asked about ni-cad's is;"should they be deep discharged
|
||
to condition the cells".Heres where that grey area starts,most manufacturers
|
||
suggest some form of deep discharge occasionally but never a total discharge.
|
||
Most devices(ie.laptops,camcorders)have internal circuitry to sense when
|
||
a battery has discharged to or near its rated capacity and disconnect either
|
||
partially or totally from the load,don't drop a load resistor across the
|
||
terminals and kill it,this will cause cell damage to one extent or another.
|
||
Most importantly begin charging shortly after you have completed discharge!
|
||
I will adress lead acid batteries later in this file,but by all means don't
|
||
deep discharge a lead acid cell,doing so will definetly harm it and possibly
|
||
destroy it.Again charging shortly after discharge is essential to long
|
||
cycle life of a lead acid battery as well.
|
||
Ni-cad chargers exist in many forms.They can be a simple as a transformer
|
||
cap and diode or as complicated as microprossesor based systems that cost
|
||
up and over $1000.The more extravigant,the better the results,usually.
|
||
The problem is when to terminate charge,overcharging a cell results in
|
||
venting.This is when a cell builds pressure internally as a result of
|
||
overcharging and releases elecrolite into the air.Over time this can cause
|
||
cell damage resulting in a significant decrease in cycle life.(# of times
|
||
a battery discharges and subsequently recharges to full capacity)
|
||
The following graph shows the voltage profile of a single ni-cad cell
|
||
during a charge cycle.
|
||
|
||
l x l x
|
||
l x l x x
|
||
l x l
|
||
l voltage x l
|
||
l x l
|
||
l x l
|
||
l x l
|
||
l x l
|
||
l x capacity l
|
||
l_______________________________________________________l______________________
|
||
0% approx 100%
|
||
|
||
Notice how the voltage peaks near full capacity and then starts to drop.
|
||
So a simple assumption would tell you that you could sense that peak
|
||
and drop (commonly referred to as the negative delta v) and terminate charge,
|
||
right?......wrong!
|
||
The promblem occurs when you put cells in series (a battery)to get appropriate
|
||
voltages.They all have slightly different voltage profiles during the charge
|
||
cycle,like this:
|
||
t1 t2
|
||
l x=cell 1 l l
|
||
l o=cell 2 l l
|
||
l t=cell 3 l o o xt x t l
|
||
l o x t o x t
|
||
l oxt o x t
|
||
lvoltage xot
|
||
l xot
|
||
l xot
|
||
l xot
|
||
l xot l ??? 100% ??? l
|
||
l xot l l
|
||
l xot capacity l l
|
||
l__________________________________________________l____________________l_______
|
||
0% l 100% l
|
||
|
||
|
||
As you can see,things get kinda grey!
|
||
|
||
This graph is unrealistic in the sense that it's impossible to determine
|
||
individual cell voltages when they are connected in series to form a battery.
|
||
What actually happens is you get a very mushy curve.If you terminate early
|
||
at position t1(see graph)most of your cells will be below full capacity,
|
||
terminate at t2 and most of them will be in overcharge.
|
||
There are a number of methods of charge termination,some simpler than
|
||
others some more effective than others,these are a few of the popular ones.
|
||
-temperature as a cell accepts current,it has a certain effeciency
|
||
at wich it turns incoming energy into stored chemical energy.(cell efficiency)
|
||
most cell systems have been optimized over the years to a point were they
|
||
are all very efficient.Were this comes into play is simple,energy in = energy
|
||
out.If a cell has reached full capacity,the incoming energy from the charging
|
||
system has to go somwhere,that somwhere is heat!So,what you can do is sense
|
||
that increase in temperature and terminate charge.sounds simple but,there
|
||
are numerous drawbacks.first of all,you have to have a temprature sensing
|
||
device in close proximity to the cells,this is impracticle in most cases.
|
||
Secondly you again have the problem of cells being different from eachother
|
||
you may terminate to early or maybe to late,your guess is as good as mine!
|
||
Lastly if your battery is located near your charging system,your near
|
||
transformers,transitors,diodes and other heat generating devices,how do you
|
||
compensate for this???
|
||
-negative delta v as discussed before,this has many drawbacks but is
|
||
the more popular among higher grade systems.
|
||
-coulometric control basically,a coulometer that keeps track of how
|
||
much energy gets discharged and then puts it back in,high cost and
|
||
inaccuracies in mesuring equipment keep this one in the ultra high
|
||
grade market.
|
||
-constant voltage don't even think about it!every manufacturer
|
||
strongly suggest anything but!
|
||
-constant current the most popular,requires alot of guess work
|
||
on the part of the manufacturer.you have to select a charge current
|
||
appropriate for capacity of the cells.To high and you overcharge,to low
|
||
and it takes you 12+ hours to reach full capacity,if at all.
|
||
combinations of any of these are also very common (exept con.v) and
|
||
can result in some nice systems.
|
||
So far I've told everything wrong with ni-cad chargers,to be truthfull
|
||
many of these can work ok.Most manufacturers claim ni-cad's can cycle up to
|
||
10,000 times if treated properly,The problem is that treated properly
|
||
means making many compromises that are unrealistic or impossible for
|
||
most applications.The last form of charging I'd like to discuss is algorithm
|
||
or "pulse" charging.It employs alot of the methods listed above,but with
|
||
a twist.
|
||
|
||
A basic pulse charge algorithm looks somthing like this:
|
||
|
||
|
||
l --------------------1 second------------------------l--next cycle-----
|
||
l l
|
||
l l
|
||
xxxxxxx----charge level 1 ---xxxxxxxxxxxxxx xxxxxxxxxxxxxxxxxx
|
||
x x
|
||
0 charge level------------------------- x xxxxxxxx -----------------
|
||
x x
|
||
x x
|
||
xxxxx ----------- -2.5 discharge
|
||
|
||
|
||
To start this a constant current charger,the output is determined by
|
||
The capacity of the cells.Charge level one represents current being passed
|
||
to the battery at a specified level.Lets say for now that that level is 1
|
||
amp.(charge level 1=1 amp)For a period of time,lets say 985ms we are putting
|
||
current into the battery.(charge level 1)After that time expires we go to
|
||
part two.(-2.5 discharge)At this point,for a short period of time,say
|
||
5ms we discharge at 2.5 times the level we charged at.(or in our case,2.5 amps)
|
||
this serves one major function,"burping".When a ni-cad cell is charging one
|
||
of the gasses being generated internaly is oxygen,it forms and sits on the
|
||
two plates of the battery.The problem happens when crystals begin to form
|
||
in the cell and use these bubbles as a bridge between the two plates(anode
|
||
and cathode)of the cell,if they complete the bridge you now have a dialectric
|
||
short,or a dead battery!What happens during that 5ms pulse or "burp" can
|
||
save alot of trouble,it breaks the bubbles and allows the oxygen to be more
|
||
readily available for the continuing chemical reaction.This accomplishes a
|
||
couple of things,as a result of the oxygen situation mentioned above you can
|
||
charge at much higher levels without cell venting.(fast charge)secondly,you
|
||
prevent shorts,giving you longer cycle life.Just as a note of interest,the
|
||
crystals that form in the cell,shorting or not,cause the chemical conversion
|
||
that takes place during charging and discharging to slow down,somtimes to a
|
||
point where the cell can't function anymore.True "memory"has yet to be proved
|
||
and this is what is really happening when your battery quits!Best way to
|
||
prevent it is to keep your battery charged when not in use.
|
||
Getting back to pulse charging,the last segment in the algorithm is
|
||
called the quiet window.It serves two basic purposes,it allows the cell
|
||
to chemically recuperate after discharging and it provides a period of time
|
||
to collect information from the cells.(such as looking for - delta v).after
|
||
the quiet window the loop begins again at charge level 1,it runs continuosly
|
||
at 1 second intervals until terminated by some method of charge termination.
|
||
Once the cell reaches near full capacity some type of maintanance charge is
|
||
usually applied,such as running an algorithym at a lower frequency and
|
||
amplitude,this helps top off the cells and keep them fully charged.
|
||
This technology is fairly new and should be introduced into the various
|
||
consumer markets soon.My only advice to people who are stuck with cheap
|
||
ni-cad chargers supplied by manufacturers is to be more selective next
|
||
time!Spending an extra $100 at purchase time will pay for itself if one
|
||
battery last you 2 years as opposed to 2 cycles.
|
||
|
||
comments or questions??
|
||
send replies to glenn sahlin
|
||
|
||
|
||
|
||
|
||
|
||
|
||
|
||
|